Did you know...

Polyurethane is the "go-to" polymer for critical film and sheet applications because it combines the toughness of rubber with the flexibility of a thermoplastic without the plasticizers.

ARGOTEC
PRODUCTS SECTION LINKS

Why Polyurethane? Product Options Table Additive Packages TPU Tech Data Tables

aromatic polyether tpu film aromatic polyester tpu film aliphatic polyether tpu film aliphatic polycaprolactone tpu film waterproof breathable film

Download Literature Order Printed Literature

Home
Products
TPU Tech Data Tables
Aromatic Polyether TPU Film

ARGOTHANE® AROMATIC POLYETHER TPU Typical Physical Properties

Argotec Number	Film Type Description	Physical Property	Test Method	Units	Test Value
17103 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: textile lamination, die cut & seal Extrusion method: blown film Gauge: 1.0-10 mils (25-250 microns) Width: up to 86 inches (2.18 meters) Length: up to 1000 non-spliced yards Smooth surface Softest ether Low softening temperature	Hardness	D-224	Shore	70 A
		Tensile stress @ 100% elongation	D-412	psi MPa	500 3.4
		Tensile stress @ 300% elongation		psi MPa	800 5.5
		Tensile strength		psi MPa	3500 24.1
		Elongation @ break		%	700
		Tensile set @ break		%	50
		Tear strength	D-624¹	pli kN/m	380 66.5
		Abrasion resistance	D-1044²	mg loss	3
17200 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: textile lamination, high MVT Extrusion method: cast film Gauge: 0.2-5 mils (5-125 microns) Width: up to 68 inches (1.73 meters) Length: up to 1000 non-spliced yards Smooth & light matte surfaces Softest ether Low softening temperature Low slip/lube	Hardness	D-224	Shore	78 A
		Tensile stress @ 100% elongation	D-412	psi MPa	450 3.1
		Tensile stress @ 300% elongation		psi MPa	695 4.8
		Tensile strength		psi MPa	3625 25
		Elongation @ break		%	860
		Tear strength	D-624¹	pli kN/m	257 45
		Abrasion resistance	D-1044²	mg loss	3
18103 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: textile lamination, medical devices Extrusion method: blown film Gauge: 1.0-10 mils (25-250 microns) Width: up to 86 inches (2.18 meters) Length: up to 1000 non-spliced yards Smooth surface Soft ether Mid-range softening temperature USP Class VI certified polymer FDA CFR 175.105	Hardness	D-224	Shore	84 A
		Tensile stress @ 100% elongation	D-412	psi MPa	900 6.2
		Tensile stress @ 300% elongation		psi MPa	1450 9.6
		Tensile strength		psi MPa	5500 37.9
		Elongation @ break		%	540
		Tensile set @ break		%	40
		Tear strength	D-624¹	pli kN/m	460 80.6
		Abrasion resistance	D-1044²	mg loss	20
18212 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: textile lamination, die cut & seal Extrusion method: flat die Gauge: 5-125 mils (125-3125 microns) Width: up to 60 inches (1.52 meters) Length: up to 1000 non-spliced yards Smooth & matte surfaces Soft ether Mid-range softening temperature USP-certified polymer FDA CFR 175.105 NSF potable water	Hardness	D-224	Shore	87 A
		Tensile stress @ 100% elongation	D-412	psi MPa	1000 6.9
		Tensile stress @ 300% elongation		psi MPa	1700 11.7
		Tensile strength		psi MPa	6200 42.7
		Elongation @ break		%	580
		Tensile set @ 200% E		%	21
		Tear strength	D-624¹	pli kN/m	435 76.2
		Abrasion resistance	D-1044⁴	mg loss	5.0
18214 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: textile lamination, bladders Extrusion method: blown film Gauge: 1.0-10 mils (25-250 microns) Width: up to 68 inches (2.18 meters) Length: up to 1000 non-spliced yards Smooth surface Soft ether Mid-range softening temperature USP-certified polymer FDA CFR 177.1680 FDA CFR 177.2600	Hardness	D-224	Shore	85 A
		Tensile stress @ 100% elongation	D-412	psi MPa	690 4.76
		Tensile stress @ 300% elongation		psi MPa	1000 6.9
		Tensile strength		psi MPa	4000 27.59
		Elongation @ break		%	700
		Tensile set @ 200% E		%	15
		Tear strength	D-624¹	pli kN/m	370 64.78
18215 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: die cut & seal Extrusion method: blown film Gauge: 1.0-10 mils (25-250 microns) Width: up to 68 inches (2.18 meters) Length: up to 1000 non-spliced yards Smooth surface Soft ether Mid-range softening temperature	Hardness	D-224	Shore	87 A
		Tensile stress @ 100% elongation	D-412	psi MPa	1000 6.89
		Tensile stress @ 300% elongation		psi MPa	1700 11.72
		Tensile strength		psi MPa	5500 37.92
		Elongation @ break		%	600
		Tensile set @ 200% E		%	15
		Abrasion Resistance	D-1044⁵	mg loss	5
18233 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: textile lamination, high MVT Extrusion method: blown film Gauge: 1.0-10 mils (25-250 microns) Width: up to 68 inches (2.18 meters) Length: up to 1000 non-spliced yards Smooth surface Harder ether Mid-range softening temperature	Hardness	D-224	Shore	90 A
		Tensile stress @ 100% elongation	D-412	psi MPa	900 6.21
		Tensile stress @ 300% elongation		psi MPa	2300 15.86
		Tensile strength		psi MPa	7000 48.26
		Elongation @ break		%	500
		Tear strength	D-624¹	pli kN/m	480 84
		MVT, 1.0 mil at RT, 50% RH	E-9613¹	g/m²/day	725
18235 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: textile lamination, die cut & seal, bladders Extrusion method: blown film Gauge: 1.0-10 mils (25-250 microns) Width: up to 68 inches (2.18 meters) Length: up to 1000 non-spliced yards Smooth surface Soft ether Mid-range softening temperature USP Class-VI polymer	Hardness	D-224	Shore	85 A
		Tensile stress @ 100% elongation	D-412	psi MPa	900 6.21
		Tensile stress @ 300% elongation		psi MPa	2300 15.86
		Tensile strength		psi MPa	7300 50.4
		Elongation @ break		%	500
		Tensile set @ 200% E		%	18
		Tear strength	D-624¹	pli kN/m	480 84
18242 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: die cut & seal, bladders Extrusion method: flat die Gauge: 5-125 mils (125-3125 microns) Width: up to 60 inches (1.52 meters) Length: up to 1000 non-spliced yards Matte 2 surfaces Soft ether Mid-range softening temperature USP Class-VI polymer	Hardness	D-224	Shore	85 A
		Tensile stress @ 100% elongation	D-412	psi MPa	990 6.8
		Tensile stress @ 300% elongation		psi MPa	1750 12.1
		Tensile strength		psi MPa	7000 48.3
		Elongation @ break		%	570
		Tensile set @ 200% E		%	13
		Tear strength	D-624¹	pli kN/m	475 83.2
		Abrasion resistance	D-1044⁵	mg loss	5
18247 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: general purpose, antistatic Extrusion method: blown film Gauge: 1.0-10 mils (25-250 microns) Width: up to 68 inches (2.18 meters) Length: up to 1000 non-spliced yards Smooth surface Soft ether Mid-range softening temperature	Hardness	D-224	Shore	85 A
		Tensile stress @ 100% elongation	D-412	psi MPa	990 6.8
		Tensile stress @ 300% elongation		psi MPa	1750 12.1
		Tensile strength		psi MPa	7000 48.3
		Elongation @ break		%	570
		Tensile set @ 200% E		%	21
		Tear strength	D-624¹	pli kN/m	475 83.2
		Abrasion resistance	D-1044⁵	mg loss	5
18248 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: industrial, UV exposure, graphics Extrusion method: blown film Gauge: 1.0-10 mils (25-250 microns) Width: up to 68 inches (2.18 meters) Length: up to 1000 non-spliced yards Smooth surface Soft ether Mid-range softening temperature UV stabilized	Hardness	D-224	Shore	85 A
		Tensile stress @ 100% elongation	D-412	psi MPa	990 6.8
		Tensile stress @ 300% elongation		psi MPa	1750 12.1
		Tensile strength		psi MPa	7000 48.3
		Elongation @ break		%	570
		Tensile set @ 200% E		%	21
		Tear strength	D-624¹	pli kN/m	475 83.2
		Abrasion resistance	D-1044⁵	mg loss	5
18305 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: industrial, textile lamination, antistatic Extrusion method: blown film nGauge: 1.0-10 mils (25-250 microns) Width: up to 86 inches (2.18 meters) Length: up to 1000 non-spliced yards Smooth surface Soft ether Mid-range softening temperature Antistatic additive	Hardness	D-224	Shore	84 A
		Tensile stress @ 100% elongation	D-412	psi MPa	900 6.2
		Tensile stress @ 300% elongation		psi MPa	2300 15.9
		Tensile strength		psi MPa	7300 54.4
		Elongation @ break		%	500
		Tensile set @ 200% E		%	18
		Tear strength	D-624¹	pli kN/m	460 84.1
18411 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: textile lamination; medical devices Extrusion method: flat die Gauge: 0.2-125 mils (5-3125 microns) Width: up to 63 inches (1.6 meters) Length: up to 1000 non-spliced yards Smooth & matte 2 surfaces Soft ether Mid-range softening temperature USP Class-VI polymer No slip/lube	Hardness	D-224	Shore	86 A
		Tensile stress @ 100% elongation	D-412	psi MPa	1100 7.6
		Tensile stress @ 300% elongation		psi MPa	1750 12.1
		Tensile strength		psi MPa	4800 33
		Elongation @ break		%	640
		Tensile set @ break		%	70
		Tear strength	D-624¹	pli kN/m	600 105
		Abrasion resistance	D-1044³	mg loss	30
		MVT1.0 mil, 38°C, 90% RH	E-968	g/m²/day	3000
18422 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: die cut & seal, bladders Extrusion method: flat die Gauge: 5-125 mils (125-3125 microns) Width: up to 60 inches (1.52 meters) Length: up to 1000 non-spliced yards Matte 2 surface Soft ether Mid-range softening temperature USP Class VI polymer	Hardness	D-224	Shore	86 A
		Tensile stress @ 100% elongation	D-412	psi MPa	1100 7.6
		Tensile stress @ 300% elongation		psi MPa	1750 12
		Tensile strength		psi MPa	4800 33
		Elongation @ break		%	640
		Tensile set @ break		%	70
		Tear strength	D-624¹	pli kN/m	600 105
		Abrasion resistance	D-1044³	mg loss	30
18433 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: textile lamination, flame resistance Extrusion method: blown film Gauge: 1.0-10 mils (25-250 microns) Width: up to 86 inches (2.18 meters) Length: up to 1000 non-spliced yards Smooth surface Soft ether Mid-range softening temperature UL-94 V2 FAR 25.853 (A)	Hardness	D-224	Shore	85 A
		Tensile stress @ 100% elongation	D-412	psi MPa	850 5.9
		Tensile stress @ 300% elongation		psi MPa	1900 13
		Tensile strength		psi MPa	7500 38
		Elongation @ break		%	595
		Tensile set @ break		%	71
		Tear strength	D-624¹	pli kN/m	500 88
		Abrasion resistance	D-1044⁵	mg loss	35
18450-FR [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: die cut & seal Extrusion method: flat die Gauge: 1.0-125 mils (25-3125 microns) Width: up to 60 inches (1.52 meters) Length: up to 1000 non-spliced yards Clear surface Soft ether Mid-range softening temperature FAR 25.853A FMVSS-302	Hardness	D-224	Shore	86 A
		Tensile stress @ 100% elongation	D-412	psi MPa	1100 7.6
		Tensile stress @ 300% elongation		psi MPa	1750 12.1
		Tensile strength		psi MPa	4800 33
		Elongation @ break		%	640
		Tensile set @ break		%	70
		Tear strength	D-624¹	pli kN/m	600 105
		Abrasion resistance	D-1044³	mg loss	30
18452-FR [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: die cut & seal Extrusion method: flat die Gauge: 5-125 mils (125-3125 microns) Width: up to 60 inches (1.52 meters) Length: up to 1000 non-spliced yards Matte 2 surface Soft ether Mid-range softening temperature FAR 25.853A FMVSS-302	Hardness	D-224	Shore	86 A
		Tensile stress @ 100% elongation	D-412	psi MPa	1100 7.6
		Tensile stress @ 300% elongation		psi MPa	1750 12.1
		Tensile strength		psi MPa	4800 33
		Elongation @ break		%	640
		Tensile set @ break		%	70
		Tear strength	D-624¹	pli kN/m	600 105
		Abrasion resistance	D-1044³	mg loss	30
19102 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: die cut & seal Extrusion method: flat die Gauge: 5-125 mils (125-3125 microns) Width: up to 60 inches (1.52 meters) Length: up to 1000 non-spliced yards Matte 2 surface Hard ether High softening temperature	Hardness	D-224	Shore	92 A
		Tensile stress @ 100% elongation	D-412	psi MPa	1430 9.9
		Tensile stress @ 300% elongation		psi MPa	2700 18.6
		Tensile strength		psi MPa	5150 35.5
		Elongation @ break		%	521
		Tear strength	D-624¹	pli kN/m	540 94.6
		Abrasion resistance	D-1044²	mg loss	50
19103 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: textile lamination Extrusion method: blown film Gauge: 1.0-10 mils (25-250 microns) Width: up to 86 inches (2.18 meters) Length: up to 1000 non-spliced yards Smooth surface Hard ether High softening temperature	Hardness	D-224	Shore	92 A
		Tensile stress @ 100% elongation	D-412	psi MPa	1430 9.9
		Tensile stress @ 300% elongation		psi MPa	2700 18.6
		Tensile strength		psi MPa	5150 35.5
		Elongation @ break		%	521
		Tear strength	D-624¹	pli kN/m	540 94.6
		Abrasion resistance	D-1044²	mg loss	50
19205 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: textile lamination Extrusion method: blown film Gauge: 1.0-10 mils (25-250 microns) Width: up to 86 inches (2.18 meters) Length: up to 1000 non-spliced yards Smooth surface Hard ether High softening temperature	Hardness	D-224	Shore	92 A
		Tensile stress @ 100% elongation	D-412	psi MPa	1430 9.9
		Tensile stress @ 300% elongation		psi MPa	2700 18.6
		Tensile strength		psi MPa	5150 35.5
		Elongation @ break		%	521
		Tear strength	D-624¹	pli kN/m	540 94.6
		Abrasion resistance	D-1044²	mg loss	50
19422 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: die cut & seal Extrusion method: flat die Gauge: 5-125 mils (125-3125 microns) Width: up to 60 inches (1.52 meters) Length: up to 1000 non-spliced yards Matte 2 surface Harder ether Highest softening temperature	Hardness	D-224	Shore	95 A
		Tensile stress @ 100% elongation	D-412	psi MPa	1750 12
		Tensile stress @ 300% elongation		psi MPa	3000 21
		Tensile strength		psi MPa	5200 36
		Elongation @ break		%	490
		Tensile set @ break		%	65
		Tear strength	D-624¹	pli kN/m	600 140
		Abrasion resistance	D-1044³	mg loss	55
19424 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: textile lamination Extrusion method: blown film Gauge: 1.0-10 mils (25-250 microns) Width: up to 86 inches (2.18 meters) Length: up to 1000 non-spliced yards Smooth surface Hardest ether Highest softening temperature	Hardness	D-224	Shore	95 A
		Tensile stress @ 100% elongation	D-412	psi MPa	1750 12
		Tensile stress @ 300% elongation		psi MPa	3000 21
		Tensile strength		psi MPa	5200 36
		Elongation @ break		%	490
		Tensile set @ break		%	65
		Tear strength	D-624¹	pli kN/m	800 140
		Abrasion resistance	D-1044³	mg loss	55
		Typical melt temperature	N/A	°C °F	198-208 388-406
19426 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: textile lamination Extrusion method: blown film Gauge: 1.0-10 mils (25-250 microns) Width: up to 86 inches (2.18 meters) Length: up to 1000 non-spliced yards Smooth surface Hardest ether Highest softening temperature No inorganic wax	Hardness	D-224	Shore	95 A
		Tensile stress @ 100% elongation	D-412	psi MPa	1750 12
		Tensile stress @ 300% elongation		psi MPa	3000 21
		Tensile strength		psi MPa	5200 36
		Elongation @ break		%	490
		Tensile set @ break		%	65
		Tear strength	D-624¹	pli kN/m	800 140
		Abrasion resistance	D-1044³	mg loss	55
		Typical melt temperature	N/A	°C °F	198-388 390-406
D7101 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: die cut & seal Extrusion method: flat die Gauge: 10-125 mils (250-3125 microns) Width: up to 60 inches (1.52 meters) Length: up to 1000 non-spliced yards Clear surface Rigid ether	Hardness	D-224	Shore	72 D
		Specific gravity	D-792	g/cc	1.20
		Tensile strength	D-638	psi MPa	10,000 69
		Elongation @ break	D-412	%	160
		Flexural modulus	D-790	psi MPa	330,000 2300

¹ Die C.
² Taber abrasion H-22 wheel, 1000 gm weight, 1000 cycles.
³ Taber abrasion H-18 wheel, 1000 gm weight, 1000 cycles.
⁴ Taber abrasion H-17 wheel, 1000 gm weight, 1000 cycles.
⁵ Taber abrasion CS-17 wheel, 1000 gm weight, 1000 cycles.