Polyurethane is the "go-to" polymer for critical film and sheet applications because it combines the toughness of rubber with the flexibility of a thermoplastic without the plasticizers.

ARGOTEC
PRODUCTS SECTION LINKS

Why Polyurethane? Product Options Table Additive Packages TPU Tech Data Tables

aromatic polyether tpu film aromatic polyester tpu film aliphatic polyether tpu film aliphatic polycaprolactone tpu film waterproof breathable film

Download Literature Order Printed Literature

Home
Products
TPU Tech Data Tables
Aromatic Polyester TPU Film

ARGOTHANE™ AROMATIC POLYESTER TPU Typical Physical Properties

Argotec Number	Film Type Description	Physical Property	Test Method	Units	Test Value
27303 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyester Uses: textile lamination Extrusion method: blown film Gauge: 1.0-10 mils (25-250 microns) Width: up to 86 inches (2.18 meters) Length: up to 1000 non-spliced yards Smooth surface Softest ester Low softening temperature	Hardness	D-224	Shore	78 A
		Tensile stress @ 100% elongation	D-412	psi MPa	600 4.1
		Tensile stress @ 300% elongation		psi MPa	1100 7.5
		Tensile strength		psi MPa	5300 36.5
		Elongation @ break		%	700
		Tensile set @ 200% E		%	60
		Tear strength	D-624¹	pli kN/m	450 78
27370 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyester Uses: elastics Extrusion method: cast film Gauge: 1.0-5 mils (25-125 microns) Width: up to 60 inches (1.52 meters) Length: up to 1000 non-spliced yards Smooth & matte surfaces Soft ester Mid-range softening temperature Low softening temperature	Hardness	D-224	Shore	78 A
		Tensile stress @ 100% elongation	D-412	psi MPa	500 3.45
		Tensile stress @ 300% elongation		psi MPa	1500 10.34
		Tensile strength		psi MPa	8000 55.16
		Elongation @ break		%	500
		Tensile set at 200% E		%	5
		Tear strength	D-624¹	pli kN/m	430 75.25
28304 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyester Uses: textile lamination Extrusion method: blown film Gauge: 1.0-10 mils (25-250 microns) Width: up to 86 inches (2.18 meters) Length: up to 1000 non-spliced yards Smooth surface Soft ester Mid-range softening temperature	Hardness	D-224	Shore	85 A
		Tensile stress @ 100% elongation	D-412	psi MPa	800 6
		Tensile stress @ 300% elongation		psi MPa	1400 10
		Tensile strength		psi MPa	6000 41
		Elongation @ break		%	600
		Tear strength	D-624¹	pli kN/m	500 88
29100 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyester Uses: textile lamination Extrusion method: blown film Gauge: 1.0-10 mils (25-250 microns) Width: up to 86 inches (2.18 meters) Length: up to 1000 non-spliced yards Smooth surface Hard ester High softening temperature	Hardness	D-224	Shore	95 A
		Tensile stress @ 100% elongation	D-412	psi MPa	1600 11
		Tensile stress @ 300% elongation		psi MPa	3500 24.1
		Tensile strength		psi MPa	6000 41.4
		Elongation @ break		%	450
		Tensile set @ 200% E		%	17
		Tear strength	D-624¹	pli kN/m	600 105.1
29102 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyester Uses: die cut & seal Extrusion method: flat die Gauge: 5-125 mils (125-3125 microns) Width: up to 60 inches (1.52 meters) Length: up to 1000 non-spliced yards Matte 2 surface Hard ester High softening temperature	Hardness	D-224	Shore	95 A
		Tensile stress @ 100% elongation	D-412	psi MPa	1600 11
		Tensile stress @ 300% elongation		psi MPa	3500 24.1
		Tensile strength		psi MPa	8000 55.2
		Elongation @ break		%	450
		Tensile set @ 200% E		%	17
		Tear strength	D-624¹	pli kN/m	600 105.1
		Abrasion resistance	D-1044⁵	mg loss	2.6
		Typical melt temperature	N/A	°C °F	185-192 365-378
29213 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyester Uses: textile lamination, die cut & seal, medical devices Extrusion method: blown film Gauge: 1.0-10 mils (25-250 microns) Width: up to 86 inches (2.18 meters) Length: up to 1000 non-spliced yards Smooth finish Hard ester High softening temperature USP Class VI FDA CFR 175.105 FDA CFR 177.1680 FDA CFR 177.2600	Hardness	D-224	Shore	90 A
		Tensile stress @ 100% elongation	D-412	psi MPa	1600 11
		Tensile stress @ 300% elongation		psi MPa	3500 24.1
		Tensile strength		psi MPa	8000 55.2
		Elongation @ break		%	450
		Tear strength	D-624¹	pli kN/m	600 105.1
		Abrasion resistance	D-1044⁵	mg loss	2.6
29222 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyester Uses: die cut & seal Extrusion method: flat die Gauge: 5-125 mils (125-3125 microns) Width: up to 60 inches (1.52 meters) Length: up to 1000 non-spliced yards Matte 2 surface Hard ester High softening temperature	Hardness	D-224	Shore	90 A
		Tensile stress @ 100% elongation	D-412	psi MPa	1600 11
		Tensile stress @ 300% elongation		psi MPa	3500 24.1
		Tensile strength		psi MPa	8000 55.2
		Elongation @ break		%	450
		Tear strength	D-624¹	pli kN/m	600 105.1
		Abrasion resistance	D-1044⁵	mg loss	2.6
29285 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyester Uses: general purpose with antistatic Extrusion method: blown film Gauge: 1.0-10 mils (25-250 microns) Width: up to 86 inches (2.18 meters) Length: up to 1000 non-spliced yards Smooth finish Hard ester High softening temperature Contains antistatic additive	Hardness	D-224	Shore	90 A
		Tensile stress @ 100% elongation	D-412	psi MPa	1600 11
		Tensile stress @ 300% elongation		psi MPa	3500 24.1
		Tensile strength		psi MPa	8000 55.2
		Elongation @ break		%	450
		Tear strength	D-624¹	pli kN/m	600 105.1
		Abrasion resistance	D-1044⁵	mg loss	2.6
29300 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyester Uses: general purpose adhesive film Extrusion method: cast film Gauge: 1.0 - 5 mils (25-125 microns) Width: up to 60 inches (1.52 meters) Length: up to 1000 non-spliced yards Smooth & matte surfaces Hard ester Low softening temperature	Hardness	D-224	Shore	90 A
		Tensile stress @ 100% elongation	D-412	psi MPa	850 5.9
		Tensile stress @ 300% elongation		psi MPa	1140 7.9
		Tensile strength		psi MPa	5900 40.7
		Elongation @ break		%	640
		Tear strength	D-624¹	pli kN/m	430 75.3

¹ Die C.
² Taber abrasion H-22 wheel (coarse), 1000 gm weight, 1000 cycles.
³ Taber abrasion H-18 wheel, 1000 gm weight, 1000 cycles.
⁴ Taber abrasion H-17 wheel, 1000 gm weight, 1000 cycles.
⁵ Taber abrasion CS-17 wheel, 1000 gm weight, 1000 cycles.