ARGOMED® TECHNICAL DATA TABLE Typical Physical Properties

Argotec Number	Film Type Description	Physical Property	Test Method	Units	Test Value
18103 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: textile lamination, medical devices Extrusion method: blown film Gauge: 1.0-10 mils (25-250 microns) Width: up to 86 inches (2.18 meters) Length: up to 1000 non-spliced yards Smooth surface Soft ether Mid-range softening temperature USP Class VI certified polymer FDA CFR 175.105	Hardness	D-224	Shore	84 A
		Tensile stress @ 100% elongation	D-412	psi MPa	900 6.2
		Tensile stress @ 300% elongation		psi MPa	1400 9.6
		Tensile strength		psi MPa	5500 37.9
		Elongation @ break		%	540
		Tensile set @ break		%	40
		Tear strength	D-624¹	pli kN/m	460 80.6
		Abrasion resistance	D-1044²	mg loss	20
18411 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyether Uses: textile lamination, medical devices Extrusion method: flat die Gauge: 0.2-125 mils (5-3125 microns) Width: up to 63 inches (1.6 meters) Length: up to 1000 non-spliced yards Smooth & matte surfaces Soft ether Mid-range softening temperature USP Class VI certified polymer No slip/lube	Hardness	D-224	Shore	86 A
		Tensile stress @ 100% elongation	D-412	psi MPa	1100 7.6
		Tensile stress @ 300% elongation		psi MPa	1750 12.1
		Tensile strength		psi MPa	4800 33
		Elongation @ break		%	640
		Tensile set @ break		%	70
		Tear strength	D-624¹	pli kN/m	600 105
		Abrasion resistance	D-1044²	mg loss	30
		MVT1.0 mil, 38°C, 90% RH	E-968	g/m²/day	3000
29102 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyester Uses: die cut & seal Extrusion method: flat die Gauge: 5-125 mils (125-3125 microns) Width: up to 60 inches (1.52 meters) Length: up to 1000 non-spliced yards Matte 2 surface Hard ester High softening temperature	Hardness	D-224	Shore	95 A
		Tensile stress @ 100% elongation	D-412	psi MPa	1600 11
		Tensile stress @ 300% elongation		psi MPa	3500 24.1
		Tensile strength		psi MPa	8000 55.2
		Elongation @ break		%	450
		Tensile set @ 200% E		%	17
		Tear strength	D-624¹	pli kN/m	600 105.0
		Abrasion resistance	D-1044³	mg loss	2.6
		Typical melt temperature	N/A	°C °F	185-192 365-378
29213 [click to download tech data sheet]	Thermoplastic polyurethane Aromatic polyester Uses: textile lamination, die cut & seal, medical devices Extrusion method: blown film Gauge: 1.0-10 mils (25-250 microns) Width: up to 86 inches (2.18 meters) Length: up to 1000 non-spliced yards Smooth finish Hard ester High softening temperature USP Class VI FDA CFR 175.105 FDA CFR 177.1680 FDA CFR 177.2600	Hardness	D-224	Shore	90 A
		Tensile stress @ 100% elongation	D-412	psi MPa	1600 11.0
		Tensile stress @ 300% elongation		psi MPa	3500 24.1
		Tensile strength		psi MPa	8000 55.2
		Elongation @ break		%	450
		Tear strength	D-624¹	pli kN/m	600 105.1
		Abrasion resistance	D-1044³	mg loss	2.6

¹ Die C.
² Taber abrasion H-22 wheel, 1000 gm weight, 1000 cycles.
³ Taber abrasion CS-17 wheel, 1000 gm weight, 1000 cycles.